Material Datasheet · ASTM / ISO StyleMaterial Datasheet · ASTM / ISO Style
鋁合金 Aluminum Alloy 5052-O
5000 Series · 鋁鎂合金系列Al-Mg Alloy Series · 退火 Annealed
1範圍 Scope
本規格表彙整鋁合金 This datasheet compiles aluminum alloy 5052-O（鋁鎂合金系列）之代表性化學成分、物理、機械、電氣、熱與加工性質。所列數值為典型參考值，依產品形式與量測條件而異，不作為設計或允收依據。's representative chemical composition, physical, mechanical, electrical, thermal, and processing properties. Values shown are typical references — they vary with product form and measurement conditions, and should NOT be used as the sole basis for design or acceptance.
2識別與國際牌號 Designations
| 材料分類Material Category | 5000 Series 鋁鎂合金系列（Al-Mg） |
| 鋁業協會 AAAluminum Association (AA) | 5052-O |
| UNS | A95052 |
| ISO | AlMg2.5 |
3化學成分 Chemical Composition (Wt. %)
| 元素 ElementElement | 含量 Composition (wt.%)Composition (wt.%) |
|---|
| 鋁 Aluminum Al | 95.7 – 97.7 |
| 鎂 Magnesium Mg | 2.2 – 2.8 |
| 其他元素（總計） Other, total — | ≤ 0.15 |
| 鉻 Chromium Cr | 0.15 – 0.35 |
| 錳 Manganese Mn | ≤ 0.1 |
| 矽 Silicon Si | ≤ 0.25 |
| 銅 Copper Cu | ≤ 0.1 |
| 其他元素（單一） Other, each — | ≤ 0.05 |
| 鋅 Zinc Zn | ≤ 0.1 |
| 鐵 Iron Fe | ≤ 0.4 |
鋁含量以餘量（remainder）計算；成分範圍為國際牌號標準值。Aluminum content is calculated as the remainder; ranges are international standard values.
4物理性質 Physical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 密度Density | 2.68 g/cc | 0.0968 lb/in³ | AA; Typical |
5機械性質 Mechanical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 硬度（布氏 HB）Hardness, Brinell | 47 | 47 | AA; Typical; 500 g load; 10 mm ball |
| 極限抗拉強度Ultimate Tensile Strength | 193 MPa | 28000 psi | AA; Typical |
| 抗拉降伏強度Tensile Yield Strength | 89.6 MPa | 13000 psi | AA; Typical |
| 斷裂伸長率Elongation at Break | 25 % | 25 % | AA; Typical; 1/16 in. (1.6 mm) Thickness |
| 斷裂伸長率Elongation at Break | 30 % | 30 % | AA; Typical; 1/2 in. (12.7 mm) Diameter |
| 彈性模數Modulus of Elasticity | 70.3 GPa | 10200 ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
| 極限承壓強度Ultimate Bearing Strength | 345 MPa | 50000 psi | Edge distance/pin diameter = 2.0 |
| 承壓降伏強度Bearing Yield Strength | 131 MPa | 19000 psi | Edge distance/pin diameter = 2.0 |
| 蒲松比Poisson's Ratio | 0.33 | 0.33 | |
| 疲勞強度Fatigue Strength | 110 MPa | 16000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| 切削加工性Machinability | 30 % | 30 % | 0-100 Scale of Aluminum Alloys |
| 剪切模數Shear Modulus | 25.9 GPa | 3760 ksi | |
| 剪切強度Shear Strength | 124 MPa | 18000 psi | AA; Typical |
6電氣性質 Electrical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 電阻率Electrical Resistivity | 4.99e-006 ohm-cm | 4.99e-006 ohm-cm | AA; Typical at 68°F |
7熱性質 Thermal Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 線膨脹係數（68°F）CTE, linear 68°F | 23.8 µm/m-°C | 13.2 µin/in-°F | AA; Typical; Average over 68-212°F range. |
| 線膨脹係數（250°C）CTE, linear 250°C | 25.7 µm/m-°C | 14.3 µin/in-°F | Average over the range 20-300ºC |
| 比熱容Specific Heat Capacity | 0.88 J/g-°C | 0.21 BTU/lb-°F | Estimated from trends in similar Al alloys. |
| 熱導率Thermal Conductivity | 138 W/m-K | 960 BTU-in/hr-ft²-°F | AA; Typical at 77°F |
| 熔點Melting Point | 607 – 649 °C | 1125 – 1200 °F | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
| 固相線溫度Solidus | 607 °C | 1125 °F | AA; Typical |
| 液相線溫度Liquidus | 649 °C | 1200 °F | AA; Typical |
8加工性質 Processing Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 退火溫度Annealing Temperature | 343 °C | 650 °F | holding at temperature not required |
| 熱加工溫度Hot-Working Temperature | 260 – 510 °C | 500 – 950 °F | |
免責聲明 DisclaimerDisclaimer本規格表數值為典型參考值，隨加工狀態、產品形式與量測條件而異，不得作為設計計算或品質允收的唯一依據。資料整理自 Aluminum Association 等公開鋁合金規格，正式設計與採購請以最新版 ASTM／ISO 標準及供應商實測報告為準。Values shown are typical references that vary with temper, product form, and measurement conditions. They must NOT be used as the sole basis for design calculations or quality acceptance. Compiled from Aluminum Association and other public aluminum specifications; for formal design and procurement, refer to the latest ASTM/ISO standards and supplier test reports.