Material Datasheet · ASTM / ISO StyleMaterial Datasheet · ASTM / ISO Style
鋁合金 Aluminum Alloy 6082-T4
6000 Series · 鋁鎂矽合金系列Al-Mg-Si Alloy Series · 熱處理 Heat-treated (T4)
1範圍 Scope
本規格表彙整鋁合金 This datasheet compiles aluminum alloy 6082-T4（6000 Series 鋁矽鎂錳合金（Al-Si-Mg-Mn））之代表性化學成分、物理、機械、電氣、熱與加工性質。所列數值為典型參考值，依產品形式與量測條件而異，不作為設計或允收依據。's representative chemical composition, physical, mechanical, electrical, thermal, and processing properties. Values shown are typical references — they vary with product form and measurement conditions, and should NOT be used as the sole basis for design or acceptance.
2識別與國際牌號 Designations
| 材料分類Material Category | 6000 Series 鋁矽鎂錳合金（Al-Si-Mg-Mn） |
| 鋁業協會 AAAluminum Association (AA) | 6082-T4 |
| ISO / EN | AlSi1MgMn (EN AW-6082 · 3.2315) |
3化學成分 Chemical Composition (Wt. %)
| 元素 ElementElement | 含量 Composition (wt.%)Composition (wt.%) |
|---|
| 鋁 Aluminum Al | 餘量 Bal. |
| 矽 Silicon Si | 0.70 – 1.30 |
| 鎂 Magnesium Mg | 0.60 – 1.20 |
| 錳 Manganese Mn | 0.40 – 1.00 |
| 鐵 Iron Fe | ≤ 0.50 |
| 鉻 Chromium Cr | ≤ 0.25 |
| 銅 Copper Cu | ≤ 0.10 |
| 鋅 Zinc Zn | ≤ 0.20 |
| 鈦 Titanium Ti | ≤ 0.10 |
| 其他（單一） — | ≤ 0.05 |
| 其他（總計） — | ≤ 0.15 |
高強度結構型擠型合金，錳提升韌性與淬火性，抗拉強度優於 6061，廣用於橋梁、車架與受力結構件。鋁含量以餘量（remainder）計算；成分範圍為國際牌號標準值。
4物理性質 Physical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 密度Density | 2.7 g/cc | 0.0975 lb/in³ | AA; Typical |
5機械性質 Mechanical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 硬度（布氏 HB）Hardness, Brinell | 70 | 70 | Typical; 500 g load; 10 mm ball |
| 硬度（維氏 HV）Hardness, Vickers | 75 | 75 | Converted from Brinell Hardness Value |
| 極限抗拉強度Ultimate Tensile Strength | 205 MPa | 29500 psi | Typical |
| 抗拉降伏強度Tensile Yield Strength | 125 MPa | 18000 psi | Typical |
| 斷裂伸長率Elongation at Break | 18 % | 18 % | Typical; 50 mm gauge length |
| 彈性模數Modulus of Elasticity | 70 GPa | 10150 ksi | Average of tension and compression |
| 剪切強度Shear Strength | 125 MPa | 18000 psi | Typical |
| 蒲松比Poisson's Ratio | 0.33 | 0.33 | Estimated from trends in similar Al alloys |
| 切削加工性Machinability | 60 % | 60 % | 0-100 Scale of Aluminum Alloys |
6電氣性質 Electrical Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 電阻率Electrical Resistivity | 3.8e-006 ohm-cm | 3.8e-006 ohm-cm | Typical at 20°C; T6 |
7熱性質 Thermal Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 線膨脹係數（20–100°C）CTE, linear | 24.0 µm/m-°C | 13.3 µin/in-°F | Average over 20-100°C range |
| 比熱容Specific Heat Capacity | 0.896 J/g-°C | 0.214 BTU/lb-°F | Typical |
| 熱導率Thermal Conductivity | 170 W/m-K | 1180 BTU-in/hr-ft²-°F | Typical; T6 |
| 熔點Melting Point | 555 – 650 °C | 1031 – 1202 °F | AA; Typical range for wrought products |
| 固相線溫度Solidus | 555 °C | 1031 °F | AA; Typical |
| 液相線溫度Liquidus | 650 °C | 1202 °F | AA; Typical |
8加工性質 Processing Properties
| 性質 PropertyProperty | 公制 MetricMetric | 英制 ImperialImperial | 備註 NotesNotes |
|---|
| 固溶處理溫度Solution Temperature | 525 °C | 977 °F | |
| 自然時效（T4）Natural Aging (T4) | — | — | 室溫自然時效 ≥ 96 hr |
免責聲明 DisclaimerDisclaimer本規格表數值為典型參考值，隨加工狀態、產品形式與量測條件而異，不得作為設計計算或品質允收的唯一依據。資料整理自 Aluminum Association 與公開文獻，正式設計與採購請以最新版 ASTM／ISO 標準及供應商實測報告為準。